| MECHANICAL PROPERTIES |
TEST METHOD |
ENGLISH XZ AXIS |
ENGLISH XZ AXIS |
METRIC ZX AXIS |
METRIC ZX AXIS |
| Tensile Strength, Yield (Type 1, 0.125”, 0.2”/min) |
ASTM D638 |
5,800 psi |
4,300 psi |
40 MPa |
30 MPa |
| Tensile Strength, Ultimate (Type 1, 0.125”, 0.2”/min) |
ASTM D638 |
8,300 psi |
6,100 psi |
57 MPa |
42 MPa |
| Tensile Modulus (Type 1, 0.125”, 0.2”/min) |
ASTM D638 |
282,000 psi |
284,000 psi |
1,944 MPa |
1,958 MPa |
| Tensile Elongation at Break (Type 1, 0.125”, 0.2”/min) |
ASTM D638 |
0.048 |
0.025 |
0.048 |
0.025 |
| Tensile Elongation at Yield (Type 1, 0.125”, 0.2”/min) |
ASTM D638 |
0.022 |
0.02 |
0.022 |
0.02 |
| Flexural Strength (Method 1, 0.05”/min) |
ASTM D790 |
13,000 psi |
9,900 psi |
89 MPa |
68 MPa |
| Flexural Modulus (Method 1, 0.05”/min) |
ASTM D790 |
291,000 psi |
261,000 psi |
2,006 MPa |
1,800 MPa |
| Flexural Strain at Break (Method 1, 0.05”/min) |
ASTM D790 |
No break |
0.04 |
No break |
0.04 |
| IZOD Impact, notched (Method A, 23°C) |
ASTM D256 |
1.4 ft-lb/in |
0.5 ft-lb/in |
73 J/m |
28 J/m |
| IZOD Impact, un-notched (Method A, 23°C) |
ASTM D256 |
16.4 ft-lb/in |
3.5 ft-lb/in |
877 J/m |
187 J/m |
| Compressive Strength, Yield (Method 1, 0.05”/min) |
ASTM D695 |
10,000 psi |
9,200 psi |
69 MPa |
64 MPa |
| Compressive Strength, Ultimate (Method 1, 0.05”/min) |
ASTM D695 |
28,000 psi |
9,400 psi |
193 MPa |
65 MPa |
| Compressive Modulus (Method 1, 0.05”/min) |
ASTM D695 |
1,100,000 psi |
227,000 psi |
7,564 MPa |
1,565 MPa |
|