| MECHANICAL PROPERTIES1 |
TEST METHOD |
ENGLISH XZ AXIS |
ENGLISH XZ AXIS |
METRIC ZX AXIS |
METRIC ZX AXIS |
| Tensile Strength, Yield (Type 1, 0.125”, 0.2”/min) |
ASTMD638 |
6,800 psi |
4,800 psi |
47 MPa |
33 MPa |
| Tensile Strength, Ultimate (Type 1, 0.125”, 0.2”/min) |
ASTMD638 |
9,950 psi |
6,100 psi |
69 MPa |
42 MPa |
| Tensile Modulus (Type 1, 0.125”, 0.2”/min) |
ASTMD638 |
312,000 psi |
329,000 psi |
2,150 MPa |
2,270 MPa |
| Tensile Elongation at Break (Type 1, 0.125”, 0.2”/min) |
ASTMD638 |
0.058 |
0.022 |
0.058 |
0.022 |
| Tensile Elongation at Yield (Type 1, 0.125”, 0.2”/min) |
ASTMD638 |
0.022 |
0.017 |
0.022 |
0.017 |
| Flexural Strength (Method 1, 0.05”/min) |
ASTMD790 |
16,200 psi |
9,900 psi |
112 MPa |
68 MPa |
| Flexural Modulus (Method 1, 0.05”/min) |
ASTMD790 |
331,000 psi |
297,000 psi |
2,300 MPa |
2,050 MPa |
| Flexural Strain at Break (Method 1, 0.05”/min) |
ASTMD790 |
No break |
0.037 |
No break |
0.037 |
| IZOD Impact, notched (Method A, 23°C) |
ASTMD256 |
2.2 ft-lb/in |
0.9 ft-lb/in |
120 J/m |
48 J/m |
| IZOD Impact, un-notched (Method A, 23°C) |
ASTMD256 |
14.6 ft-lb/in |
3.2 ft-lb/in |
781 J/m |
172 J/m |
| Compressive Strength, Yield (Method 1, 0.05”/min) |
ASTMD695 |
14,500 psi |
12,700 psi |
100 MPa |
87 MPa |
| Compressive Strength, Ultimate (Method 1, 0.05”/min) |
ASTMD695 |
26,200 psi |
13,100 psi |
181 MPa |
90 MPa |
| Compressive Modulus (Method 1, 0.05”/min) |
ASTMD695 |
1,030,000 psi |
251,000 psi |
7,012 MPa |
1,731 MPa |
|