| TEST METHOD |
STANDARD |
XZ Orientation |
ZX Orientaton |
| Tension Strength, Yield (Type 1, 0.125 in., 0.2 in./min) |
ASTM D638 |
93.1 ± 0.4 MPa(13,504 ± 57 psi) |
45.9 ± 5.3 MPa（6,650 ± 765 psi) |
| Tensile Strength, Ultimate (type 1, 0.125 in., 0.2 in./min) |
ASTM D638 |
93.1 ± 0.4 MPa(13,504 ± 57 psi) |
45.9 ± 5.3 MPa(6,650 ± 765 psi) |
| Tensile Modulus (Type 1, 0.125 in., 0.2 in./min) |
ASTM D638 |
3.1 ± 0.3 GPa(448.9 ± 39.5 ksi) |
3.5 ± 0.7 GPa(505.3 ± 108.2 ksi) |
| Elongation at Break (Type 1, 0.125 in., 0.2 in./min) |
ASTM D638 |
6.40 ± 1.05%1 |
1.22 ± 0.28%1 |
| Elongation at Yield (Type 1, 0.125 in., 0.2 in./min) |
ASTM D638 |
4.31 ± 0.58% |
1.11 ± 0.53%2 |
| Flexural Strength (Method 1, 0.05 in./min) |
ASTM D790 |
142 ± 3 MPa(20,548 ± 477 psi) |
64 ± 10 MPa(9,349 ± 1,514 psi) |
| Flexural Modulus (Method 1, 0.05 in./min) |
ASTM D790 |
3.1 ± 0.1 GPa(445.6 ± 10.8 ksi) |
2.7 ± 0.1 GPa(388.7 ± 13.0 ksi) |
| Flexural Strain at Break (Method 1, 0.05 in./min) |
ASTM D790 |
No break |
2.41 ± 0.39%3 |
| Notched Impact (Method A, 23 °C) |
ASTM D256 |
37 ± 6 J/m(0.69 ± 0.12 ft-lb/in) |
27 ± 5 J/m(0.51 ± 0.09 ft-lb/in) |
| Unnotched Impact (Method A, 23°C) |
ASTM D256 |
1,826 ± 1,254 J/m |
75 ± 28 J/m |
| Compressive Strength, Yield (Method 1, 0.05 in./min)(Method 1, 0.05 in./min) |
ASTM D695 |
100 ± 2 MPa(14,572 ± 317 psi) |
101 ± 3 MPa(14,595 ± 439 psi) |
| Compressive Strength, Ultimate (Method 1, 0.05 in./min) |
ASTM D695 |
100 ± 2 MPa(14,572 ± 317 psi) |
101 ± 3 MPa(14,595 ± 439 psi) |
| Compressive Modulus (Method 1, 0.05 in./min) |
ASTM D695 |
2.45 ± 0.01 GPa(355.6 ± 1.6 ksi) |
2.3 ± 0.1 GPa(336.3 ± 12.1 ksi) |
|
| TEST METHOD |
STANDARD |
XZ Orientation |
ZX Orientaton |
| Tensile Strength, Yield (Type 1, 0.125 in., 0.2 in./min |
ASTM D638 |
90.6 ± 3.0 MPa(13,138 ± 438 psi) |
57.0 ± 5.0 MPa(8,265 ± 718 psi) |
| Tensile Strength, Ultimate (Type 1, 0.125 in., 0.2 in./min) |
ASTM D638 |
90.6 ± 3.0 MP(13,138 ± 438 psi) |
57.0 ± 5.0 MPa(8,265 ± 718 psi) |
| Tensile Modulus (Type 1, 0.125 in.m 0.2 in..min) |
ASTM D638 |
2.92 ± 0.10 GPa(423.8 ± 15.1 ksi) |
2.86 ± 0.18 GPa(415.4 ± 26.3 ksi) |
| Elongation at Break (Type 1, 0.125 in., 0.2 in./min) |
ASTM D638 |
6.08 ± 1.31%1 |
1.87 ± 0.30% |
| Elongation at Yield (Type 1, 0.125 in., 0.2 in./min) |
ASTM D638 |
4.26 ± 0.32% |
1.78 ± 0.45%2 |
| Flexural Strength (Method 1, 0.05 in./min) |
ASTM D790 |
140.0 ± 3.9 MPa(25,299 ± 569 psi) |
87.9 ± 14.4 MPa(12,743 ± 2,083 psi) |
| Flexural Modulus (Method 1, 0.05 in./min) |
ASTM D790 |
3.07 ± 0.06 GPa(445.2 ± 9.1 ksi) |
2.73 ± 0.08 GPa(395.8 ± 12.2 ksi) |
| Flexural Strain at Break (Method 1, 0.05 in./min) |
ASTM D790 |
4.55 ± 0.37%3 |
3.3 ± 1.90%4 |
| Notched Impact (Method A, 23 °C) |
ASTM D256 |
44 ± 4 J/m(0.83 ± 0.07 ft-lb/in) |
33 ± 9 J/m(0.61 ± 0.16 ft-lb/in) |
| Unnotched Impact (Method A, 23 °C) |
ASTM D256 |
1,553 ± 464 J/m(29.1 ± 8.7 ft-lb/in) |
153 ± 40 J/m(2.86 ± 0.74 ft-lb/in) |
| Compressive Strength, Yield (Method 1, 0.05 in./min) |
ASTM D695 |
97.5 ± 3.1 MPa(14,135 ± 445 psi) |
93.5 ± 2.9 MPa(13,559 ± 417 psi) |
| Comrpessive Strength, Ultimate (Method 1, 0.05 in./min) |
ASTM D695 |
97.5 ± 3.1 MPa(14,135 ± 445 psi) |
93.5 ± 2.9 MPa(13,559 ± 417 psi) |
| Compressive Modulus (Method 1, 0.05 in./min) |
ASTM D695 |
2.36 ± 0.05 GPa(341.5 ± 7.5 ksi) |
2.18 ± 0.06 GPa(316.7 ± 9.2 ksi) |
|
|