MECHANICAL PROPERTIES1 |
TEST METHOD |
ENGLISH XZ AXIS |
ENGLISH XZ AXIS |
METRIC ZX AXIS |
METRIC ZX AXIS |
Tensile Strength, Yield (Type 1, 0.125”, 0.2”/min) |
ASTM D638 |
9,300 psi |
6,100 psi |
64 MPa |
42 MPa |
Tensile Strength, Ultimate (Type 1, 0.125”, 0.2”/min) |
ASTM D638 |
11,700 psi |
5,400 psi |
81 MPa |
37 MPa |
Tensile Modulus (Type 1, 0.125”, 0.2”/min) |
ASTM D638 |
402,000 psi |
322,000 psi |
2,770 MPa |
2,200 MPa |
Tensile Elongation at Break (Type 1, 0.125”, 0.2”/min) |
ASTM D638 |
0.033 |
0.02 |
0.033 |
0.02 |
Tensile Elongation at Yield (Type 1, 0.125”, 0.2”/min) |
ASTM D638 |
0.022 |
0.015 |
0.022 |
0.015 |
Flexural Strength (Method 1, 0.05”/min) |
ASTM D790 |
21,000 psi |
11,100 psi |
144 MPa |
77 MPa |
Flexural Modulus (Method 1, 0.05”/min) |
ASTM D790 |
409,000 psi |
324,000 psi |
2,820 MPa |
2,230 MPa |
Flexural Strain at Break (Method 1, 0.05”/min) |
ASTM D790 |
No break |
0.035 |
No break |
0.035 |
IZOD Impact, notched (Method A, 23°C) |
ASTM D256 |
0.8 ft-lb/in |
0.4 ft-lb/in |
41 J/m |
24 J/m |
IZOD Impact, un-notched (Method A, 23°C) |
ASTM D256 |
6.1 ft-lb/in |
2.6 ft-lb/in |
326 J/m |
138 J/m |
Compressive Strength, Yield (Method 1, 0.05”/min) |
ASTM D695 |
19,500 psi |
15,100 psi |
134 MPa |
107 MPa |
Compressive Strength, Ultimate (Method 1, 0.05”/min) |
ASTM D695 |
No break |
15,500 psi |
No break |
1,125 MPa |
Compressive Modulus (Method 1, 0.05”/min) |
ASTM D695 |
1,450,000 psi |
305,000 psi |
10,000 MPa |
1,120 MPa |
THERMAL PROPERTIES2 |
TEST METHOD |
ENGLISH |
METRIC |
Heat Deflection (HDT) @ 66 psi, 0.125” unannealed |
ASTM D648 |
421°F |
216°C |
Heat Deflection (HDT) @ 264 psi, 0.125” unannealed |
ASTM D648 |
415°F |
213°C |
Vicat Softening Temperature (Rate B/50) |
ASTM D1525 |
416°F |
214°C |
Glass Transition Temperature (Tg) |
DSC (SSYS) |
419°F |
215°C |
Coefficient of Thermal Expansion |
ASTM E831 |
26x10-06 in/(in·°F) |
47 µm/(m·°C) |
Coefficient of Thermal Expansion (xflow) |
ASTM E831 |
25x10-06 in/(in·°F) |
41 µm/(m·°C) |
Melting Point |
--------------- |
Not Applicable3 |
Not Applicable3 |
ELECTRICAL PROPERTIES |
TEST METHOD |
VALUE RANGE |
Volume Resistivity |
ASTM D257 |
1.0 x1014 - 8.96x1015 ohm-cm |
Dielectric Constant |
ASTM D150-98 |
2.67 |
Dissipation Factor |
ASTM D150-98 |
0.001 |
Dielectric Strength |
ASTM D149-09, Method A |
240 V/mil |
|